3DXSTAT ESD PETG

Ref.: 3DXTECH-PETG-ESD-175-750

110.00 €

-10%

99.00 €

Tax excl.

Diameter

Format

Quantity

In stock 14 units available for immediate shipping.
units available for shipping in 10 - 15 days Available for shipment within 10 - 15 days

Product temporarily out of stock with these characteristics. Select another combination.

We notify you when it will be available:

Approximate delivery date: Friday 15 November

Available

Returns

Ask about this product

PETG ESD filament is one of the materials offered by 3DXtech, a renowned North American manufacturer specialising in technical filaments for professional applications.

PETG ESD filament is a filament specifically developed for applications requiring electrostatic discharge protection and good chemical resistance. Manufactured from high-flux PETG and CNT for exceptional repeatability and reliability.

Manufactured with state-of-the-art multi-wall carbon nanotube technology, its surface resistance is 10^7 to 10^9 Ohm.

Due to its high PETG content, this filament retains many of the properties of PETG:

Ease of printing.
Wide printing temperature range: 230-260 ºC.
Does not require the use of a hot bed.
Low shrinkage, almost no warping effect.
Chemical resistance superior to ABS.
Low moisture absorption.
Low odour - ideal for printing in office environments.

In addition, PETG ESD has other very interesting properties that make it stand out from other ESD materials:

Consistent and reliable surface strength.
Better impact retention and elongation than similar ESD-safe materials.
Low particulate contamination.
Minimal contribution to outgassing and ionic contamination.

PETG ESD has good resistance to dilute aqueous solutions of mineral acids, bases, salts and soaps, and to aliphatic hydrocarbons, alcohols and a variety of oils. Halogenated hydrocarbons, short chain ketones and aromatic hydrocarbons dissolve or swell the plastic.

PLA ESD filament is ideal for the manufacture of hard disk drive components, housings or connectors, as well as for industrial applications such as device manufacturing, transportation, measurement, end-of-arm tooling and sensing applications.

Resistance according to printing temperature

Image 1: Surface resistance according to printing temperature of PETG ESD. Source: 3DXTech.

In order to achieve the highest possible electrostatic conductivity, it is recommended to use the highest possible extrusion temperature recommended by the manufacturer (260 °C).

General information
Material	PETG
Format	50 g / 1000 g
Density	(ISO 1183) 1.28 g/cm³
Filament diameter	1.75 / 2.85 mm
Filament tolerance	± 0.05 mm
Filament length	(Ø 1.75mm - 1 Kg) ± 324 / (Ø 2.85mm - 1 Kg) ± 122

Electrical properties
Surface electrical resistivity	10⁷ - 10⁹ Ohm/sq

Printing properties
Printing temperature	230 - 260 ºC
Print bed temperature	70 ºC
Chamber temperature	-
Cooling fan	✓
Recommended printing speed	- mm/s

Mechanical properties
Elongation at break	(ISO 527) 13 %
Tensile strength	(ISO 527) 50 MPa
Tensile modulus	(ISO 527) 1800 MPa
Flexural strength	(ISO 178) 74 MPa
Flexural modulus	(ISO 178) 1780 MPa
Surface hardness	-
Impact strength	3 KJ/m²

Thermal properties
Softening temperature	(ASTM E2092) 80 ºC

Specific properties
Transparency	-
Chemical resistance	✓

Other
HS Code	3916.9
Spool diameter (outer)	200 mm
Spool diameter (inner hole)	53 mm
Spool width	50 mm

PETG ESD filament has the printability of PETG. The recommended printing temperature is between 230 and 260°C. PETG ESD is a filled product and has a higher melt viscosity compared to unfilled PETG. Therefore, it is sometimes necessary to print at higher temperatures than standard PETG to allow the material to flow properly.

Resistivity is greatly affected by temperature and printing speed. In case the resistivity values of the part are too high, it is recommended to increase the printing temperature and reduce the speed.

As with standard PETG, this material does not require the use of a heated bed, although if available, it is recommended to use it at a temperature between 60 and 90°C. The use of the coating fan is recommended for an optimum finish.

Although not prone to warping, Magigoo or Dimafix can be used to improve adhesion to the base.

With PETG ESD it is not necessary to use reinforced nozzles as this filament has low abrasion, but nozzles with output diameters of 0.5 mm or more are recommended to avoid clogging.

If you have an FDM 3D printer with a double extruder and you need to 3D print complex parts, it is possible to use this material in combination with X1 support, a hot water soluble material.