3843 HDT60 High Toughness black resin - Loctite 3D

Compare

You must be logged in to manage your wishlist.

3843 Resin - Loctite 3D

Ref.: RS-LOC-3843-HDT60-MATTEBLACK-1KG

180.00 €

Tax excl.

Format

Colour

Quantity

In stock 11 units available for immediate shipping.
units available for shipping in 4 - 6 days Available for shipment within 4 - 6 days

Product temporarily out of stock with these characteristics. Select another combination.

We notify you when it will be available:

Approximate delivery date: Wednesday 16 October

Available

Returns

Ask about this product

The 3843 HDT60 High Toughness resin from the Loctite family of high impact resistant resins is a semi-flexible ABS-like resin that prints parts characterized by a great surface finish, moderate temperature resistance (HDT of 63 ºC), as well as elevated impact strength. This material is available in the following colors: white, translucid, and matte black.

Video 1: 3843 HDT60 High Toughness resin. Source: Loctite.

The 3843 HDT60 High Toughness resin is adequate for uses in tooling applications, in the 3D printing of housings and covers, jigs and fixtures, as well as various manufacturing aids. The ideal sectors for this material are industrial, automotive and consumer goods.

The 3843 HDT60 High Toughness resin has been formulated to print optimally on industrial DLP printers. Before printing with this material, the user should read safety and technical information available in the Downloads section. In the Usage Tips section useful resources can be found on printer compatibility, recommended post-processing settings, and proper resin storage.

Curing, washing, and sintering properties
Washing time	2 min
Curing time	2 - 20 min

General information
Manufacturer	Loctite
Material	Photopolymer
Format	1 kg / 5 kg
Technology	DLP/LCD
Wavelength	- nm
Viscosity	(ASTM D7867) 720-870 cP
Density (solid)	(ASTM D1475) 1.18 g/cm³
Density (liquid)	(ASTM D1475) 1.07 g/cm³

Printing properties
Layer height	- µm
Layer exposure time	-
Layer off time	-
Lifting height	- mm
Bottom layer exposure	-
Bottom layer count	-

Mechanical properties
Izod impact strength	- KJ/m²
Charpy impact strength	- KJ/m²
Elongation at break	(ASTM D638) 43 ± 10 %
Tensile strength	(ASTM D638) 53 ± 2 MPa
Tensile modulus	(ASTM D638) 1806 ± 47 MPa
Flexural strength	- MPa
Flexural modulus	(ASTM D790) 1783 ± 45 MPa
Surface hardness	(ASTM D2240) Shore 67-74 D

Electrical properties
Volumetric resistivity	(ASTM D257) 6.5E ± 14 Ω/cm
Surface electrical resistivity	(ASTM D257) 5.7E ± 15 Ω
Dielectric strength	(ASTM D149) 28.1 ± 1.8 kV/mm
Dissipation factor	(ASTM D150) 0.021
Permittivity	(ASTM D150) 4.4-4.9

Thermal properties
Softening temperature	63 ºC
Heat deflexion temperature	(ASTM D648) 63 ºC
Thermal expansion coefficient	(ASTM E831) 10-60 ºC: 131.9 µm/(m·K)
Thermal conductivity	(ASTM D5930) 0.21 W/(m·K)

Specific properties
Maximum water absorption	(ASTM D570) 24 h: 1.94 % / 72 h: 3.21 %

Other
HS Code	2916.1
Lifetime (since manufacturing)	- M

On the Henkel YouTube channel, various videos are available on:

How to work with 3D printing resins:
Video 1: The basics of printing with resin. Source: Henkel.
How to properly store 3D printing resins:
Video 2: How to properly store resins. Source: Henkel.
How to post-process parts 3D printed with resin:
Video 3: Resin post-processing tips. Source: Henkel.

The material's technical and safety datasheets can be found in the Downloads section. On the manufacturer's website the user can find the printer validation information as well as the recommended printing and postprocessing settings.