3172 resin - Loctite 3D

Ref.: RS-LOC-3172-HDT50-GREY-1KG

180.00 €

Tax excl.

Format

Colour

Quantity

In stock 3 units available for immediate shipping.
units available for shipping in 4 - 6 days Available for shipment within 4 - 6 days

Product temporarily out of stock with these characteristics. Select another combination.

We notify you when it will be available:

Approximate delivery date: Friday 27 December

Available

Returns

Ask about this product

The 3172 HDT50 High Impact resin from the Loctite family of high impact resins is a strong and durable resin with mechanical properties similar to polypropylene. Apart from being characterized by great elongation at break, excellent impact strength and compression strength, parts 3D printed with the 3172 HDT50 resin can be machined, tapped or polished to further enhance their visual aspect. The 3172 HDT50 High Impact resin is the perfect material for the additive manufacturing of tooling, manufacturing aids, housings, shoe insoles, and many more.

3D printed parts with 3172 HDT50 High Impact resin in gray color

Image 1: 3D printed parts with 3172 HDT50 High Impact resin in gray color. Source: Loctite.

The 3172 HDT50 High Impact resin has been formulated to print optimally on industrial DLP printers. Before printing with this material, the user should read safety and technical information available in the Downloads section. In the Usage Tips section useful resources can be found on printer compatibility, recommended post-processing settings, and proper resin storage.

Curing, washing, and sintering properties
Washing time	2 min
Curing time	-
Curing temperature	- ºC

General information
Manufacturer	Loctite
Material	Photopolymer
Format	1 kg / 5 kg
Technology	DLP/LCD
Wavelength	- nm
Viscosity	(ASTM D7867) 1700-2000 cP
Density (solid)	(ASTM D792) 1.0-1.4 g/ml
Density (liquid)	(ASTM D1475) 1.1 g/cm³

Printing properties
Layer height	- µm
Layer exposure time	-
Layer off time	-
Lifting height	- mm
Bottom layer exposure	-
Bottom layer count	-

Mechanical properties
Izod impact strength	- KJ/m²
Charpy impact strength	- KJ/m²
Elongation at break	(ASTM D638) 141 ± 4 %
Tensile strength	(ASTM D638) 38 ± 1.4 MPa
Tensile modulus	(ASTM D638) 1245 ± 43 MPa
Flexural strength	(ASTM D790) 37.6 ± 2.56 MPa
Flexural modulus	(ASTM D790) 1022 ± 76 MPa
Surface hardness	(ASTM D2240) Shore 70 D

Thermal properties
Softening temperature	52 ºC
Heat deflexion temperature	(ASTM D648) @ 0.45 MPa: 51 ± 0.7 ºC
Thermal expansion coefficient	(ASTM E831) 171 ± 4 µm/(m·K)
Thermal conductivity	(ASTM D5930) 199 mW/(m·K)

Specific properties
Maximum water absorption	(ASTM D570) 24 h: 1.4-1.6 % / 72 h: 2.4-2.6 %

Other
HS Code	2916.1
Lifetime (since manufacturing)	- M

On the Henkel YouTube channel, various videos are available on:

How to work with 3D printing resins:
Video 1: The basics of printing with resin. Source: Henkel.
How to properly store 3D printing resins:
Video 2: How to properly store resins. Source: Henkel.
How to post-process parts 3D printed with resin:
Video 3: Resin post-processing tips. Source: Henkel.

The material's technical and safety datasheets can be found in the Downloads section. On the manufacturer's website the user can find the printer validation information as well as the recommended printing and postprocessing settings.