xFLEX402-Black resin Nexa 3D

RS-NEXA-XFLEX402-BLACK-1000
295.00 € 295.00 €
Tax excl.
Format
Quantity

In stock 0 units available for immediate shipping.
units available for shipping in 5 - 9 days Available for shipment within 5 - 9 days

Product temporarily out of stock with these characteristics. Select another combination.

Product temporarily out of stock with these characteristics. Select another combination.

We notify you when it will be available:

Approximate delivery date: Friday 22 November - Thursday 28 November
Available

Nexa 3D and Henkel have partnered yet again to create the single-component xFLEX402-Black 3D printing resin. This material is a semi-firm rubberlike elastomer that produces durable parts with high rebound, great elongation at break (230 %), excellent tensile strength and high energy return (30-35 %).

A flexible shoe insole 3D printed with the xFLEX402 resin

Image 1: A flexible shoe insole 3D printed with the xFLEX402 resin. Source: Nexa 3D.

The xFLEX402-Black resin is optimized to be used on the Nexa 3D printers, including the first Nexa 3D desktop solution - the ultrafast 4K XiP printer that uses the patented Nexa 3D LSPc technology to deliver highly accurate parts with great surface properties and isotropic properties.

Video 1: Working with the xFLEX402-Black resin. Source: Nexa 3D.

Thus, prototypes and end-use parts for many sectors (footwear design and production, tools, etc) can be 3D printed with the xFLEX402 resin, with fast and reliable results guaranteed for a more agile and independent production workflow and supply chain.

Curing, washing, and sintering properties
Washing time -
Curing time -
Curing temperature - ºC

General information
Manufacturer Nexa 3D
Material Photopolymer
Format 1 kg
Technology LED / LCD
Wavelength - nm
Compatible 3D printers Nexa 3D

Printing properties
Layer height - µm
Layer exposure time -
Layer off time -
Lifting height - mm
Bottom layer exposure -
Bottom layer count -

Mechanical properties
Izod impact strength - KJ/m²
Charpy impact strength - KJ/m²
Elongation at break (ASTM D638M) 230 %
Tensile strength (ASTM D638M) 5.5 MPa
Tensile modulus (ASTM D638M) 42 MPa
Flexural strength - MPa
Flexural modulus - MPa
Surface hardness (ASTM D2240) Shore 73 A

Thermal properties
Softening temperature - ºC

Specific properties
Maximum water absorption (ASTM D570) 3.15 %

Other
HS Code 2916.1
Lifetime (since manufacturing) - M

Parts 3D printed with the Nexa 3D xFLEX402 resin will achieve their specific properties only after being subjected to post-processing by washing and curing. If applicable, the support structures must be removed from the part before curing and the part must be washed. The xFLEX402 resin is a plant-based material which allows for washing the 3D printed parts in water, combined with soft brushing. This means that no IPA alcohol or other substances are needed for the washing of this material but the Nexa 3D xClean can be used.

Once washed, the parts 3D printed with the xFLEX402 resin must be dried and then cured either with the help of an LED or wide spectrum lamp, or in the Nexa 3D Wash+Cure station developed especially for the washing and curing of parts 3D printed on the XiP 3D printer. The recommended washing, drying and curing times can be consulted on the manufacturer's website for each Nexa 3D resin.

Certain precautions must be taken when working with 3D printing resins. The user must ensure that the working space is adequately ventilated, and that protective goggles, gloves and garments are worn at all times. The xFLEX402 resin should be stored in a tightly closed container/resin vat to avoid resin deterioration due to UV exposure. The container/vat should be kept in a cool, well ventilated area away from heat, sparks and open flame.

More information on how to print and post-process the Nexa 3D resins can be found here.

Featured properties

Technology
LED / LCD

Related products