Liqcreate Composite-X resin

Ref.: LIQC-COMPOSITEX-375

58.95 €

Tax excl.

Format

Quantity

In stock 1 units available for immediate shipping.
units available for shipping in 3 - 4 days Available for shipment within 3 - 4 days

Product temporarily out of stock with these characteristics. Select another combination.

We notify you when it will be available:

Approximate delivery date: Friday 27 December

Available

Returns

Ask about this product

The Composite-X resin from the catalog of engineering resins by Liqcreate is an extremely rigid and high performance nano-micro composite reinforced resin for SLA, DLP and LCD/MSLA 3D printing. With a flexural modulus of around 9000 MPa and a flexural strength of up to 170 MPa (with thermal post-curing), the Composite-X resin is superior to almost all photopolymer resins currently available on the market.

Video 1: Presenting the Composite-X resin. Source: Liqcreate.

Apart from the high rigidity, the Composite-X resin is characterized by high strength and great chemical resistance, as well as extremely low shrinkage and odor during printing. All these properties make the Composite-X resin the perfect material not only for rapid tooling but also for heavy duty industrial or automotive applications, wind tunnel testing, fluid flow components, etc.

A swingarm 3D printed with the Composite-X resin

Image 1: A swingarm 3D printed with the Composite-X resin. Source: Liqcreate.

The Composite-X is easy to use on all open SLA, DLP and compatible LCD/MSLA 3D-printers in the range of 385-420 nm by brands such as Anycubic, Phrozen or Creality. A full list of compatible printers can be consulted on the manufacturer's website.

A gear 3D printed with the Composite-X resin

Image 2: A gear 3D printed with the Composite-X resin. Source: Liqcreate.

It should be kept in mind that the Composite-X resin is intended for advanced users. Furthermore, the Composite-X resin can have an abrasive effect on aluminum parts due to the ceramic particles it contains. This is why it is highly recommended to use anodized aluminum or coated aluminum resin tanks when working with the Composite-X resin. More advice on printing with the Composite-X resin can be found in this article on the manufacturer's website.

Curing, washing, and sintering properties
Washing time	4 - 5 min
Curing time	-
Curing temperature	- ºC

General information
Manufacturer	Liqcreate
Material	Photopolymer
Format	0.375 kg / 1.5 kg
Technology	SLA / LED-LCD / DLP
Wavelength	385 - 405 nm
Viscosity	@ 25 ºC: 1400 cP
Density (solid)	1.62 g/cm³
Density (liquid)	1.52 g/cm³

Printing properties
Layer height	50 - 100 µm
Layer exposure time	-
Layer off time	-
Lifting height	- mm
Bottom layer exposure	-
Bottom layer count	-

Mechanical properties
Izod impact strength	- KJ/m²
Charpy impact strength	- KJ/m²
Elongation at break	(ASTM D638M) 1 %
Tensile strength	(ASTM D638M) 50 - 75 MPa
Tensile modulus	(ASTM D638M) 7500 - 8500 MPa
Flexural strength	(ASTM D790) 140 - 150 MPa
Flexural modulus	(ASTM D790) 7500 - 8500 MPa
Surface hardness	(ASTM D2240) Shore 93 D
Compressive strength	(D695) 155-160 MPa

Thermal properties
Softening temperature	86 ºC

Specific properties
Maximum water absorption	(D570-98) 0.59-0.67 %

Other
HS Code	2916.1
Lifetime (since manufacturing)	- M

In order to ensure resin longevity and successful 3D prints, it is advised to store the Composite-X resin in a clean and dry environment, out of direct sunlight and in a temperature of 5-30 ºC. Before use, the resin bottle should be shaken energetically for at least 1 minute (at least 3 minutes in the case of filled resins) and then left to rest for around 10 minutes to let the air bubble escape. Leftover resin can be poured back into the bottle but it should be first filtered to ensure there is no polymer residue present. Safety equipment such as protective garments, gloves and face protection is highly recommended for the handling of resin.

As far as the post-processing of the Composite-X resin, a few simple steps must be followed. First, the 3D printed part has to be cleaned for a maximum of 6 minutes in Liqcreate Resin Cleaner, IPA alcohol or bioethanol, preferably ultrasonic or under agitation. Then the completely dried part has to be cured in a high-power UV curing chamber. The curing workflow is explained in detail by the manufacturer here. It absolutely crucial that the parts are dry before they are cured. The curing of wet or sticky parts will lead to mechanical and surface defects. The drying can be done by simply leaving the cleaned part in a well ventilated area for at least 30 minutes or with the help of pressurized air (2 minutes) for parts cleaned in IPA alcohol or ethanol.