Model Resin - HARZ Labs

Ref.: MODEL-HL-LCD-BLACK-1000

89.00 €

Tax excl.

Colour

Technology

Quantity

In stock 2 units available for immediate shipping.
units available for shipping in 7 - 10 days Available for shipment within 7 - 10 days

Product temporarily out of stock with these characteristics. Select another combination.

We notify you when it will be available:

Approximate delivery date: Thursday 26 December

Available

Returns

Ask about this product

HARZ Labs Model Resin is a resin for all types of 3D resin printers developed to print parts that need to withstand great mechanical stress.

HARZ Labs is a resin manufacturer with extensive experience in chemical products, especially polymers, which develops and produces high quality materials for all types of 3D resin printer technologies (DLP / LCD, SLA, CJP and others).

HARZ Labs Model Resin is developed to offer the best mechanical properties while maintaining great ease of printing. One of the highlights of this resin is the low contraction, less than 0.5%, contraction that the parts suffer during the manufacturing process, thus obtaining very precise models in a simple way.

Dinosaur printed with Model Grey resin

Image 1: Dinosaur printed with Model Grey resin. Source: HARZ Labs.

HARZ Labs Model Resin has a Shore D hardness of 85-92 but at the same time shows elasticity, really useful properties for printing durable and non-fragile models, such as semi-permanent molds for melting rubber. This is also possible thanks to its high heat resistance, withstanding long working intervals with temperatures up to 100 °C or 180 °C for short-term work. If all this is not necessary, HARZ Labs Model Resin has a wide range of colors and its lighter models (white, gray and etc.) can be modified with certain dyes to achieve the color desired by the user.

Parts printed with Model resin

Image 2: Parts printed with Model resin. Source: HARZ Labs.

In the section on printing properties, its relatively low density stands out, which provides high precision for short printing times, as well as facilitating the time spent cleaning the printer. Unlike other universal resins on the market, HARZ Labs Model Resin is odorless and does not cause irritation, so it can be used in any space that has natural ventilation, without the need for forced ventilation. This is due to the fact that this resin does not contain volatile components such as solvents, monomers or other irritant compounds. Another rare advantage is its great stability, since the resin can be left in the tank for long periods of time without sedimentation or gelatinous areas.

The properties of Model resin

Image 3: The properties of Model resin. Source: HARZ Labs.

All the previous properties make HARZ Labs Model Resin a very interesting material to manufacture final pieces that need to withstand great efforts. But this is not all, the biggest advantage of all is that this resin is universal, since it is available for 3D resin printers that use SLA (Form 2) or LCD / DLP technology making it easier for users to find new alternatives to print any Type of part in any type of 3D resin printer: Formlabs, PEOPOLY, UniZ, WANHAO, zortrax, ANYCUBIC, ASIGA, B9 Creator, FLASH FORGE Moon Ray, PRUSA.

Curing, washing, and sintering properties
Washing time	5 - 15 min
Curing time	15 - 60 min

General information
Manufacturer	HARZ Labs
Material	Photopolymer
Format	0.5 kg / 1 kg
Technology	SLA / LED-LCD / DLP
Wavelength	UV 405 nm
Viscosity	(ASTM D2393) @ 20-25 ºC: 150-1000 mPa·s
Density (solid)	(ASTM D1298) 1.06-1.1 g/cm³

Printing properties
Layer height	100 / 50 / 25 µm
Layer exposure time	-
Layer off time	-
Lifting height	- mm
Bottom layer exposure	-
Bottom layer count	-

Mechanical properties
Izod impact strength	(ASTM D4812) Model White LCD/DLP: 5.7 ± 0.2 / Model Clear LCD/DLP: 4.4 ± 0.2 / Model Grey LCD/DLP: 5.7 ± 0.2 / Model Black LCD/DLP: 4.1 ± 1.1 / Model White SLA: 5.4 ± 0.2 / Model Clear SLA: 4.1 ± 1.2 / Model Grey SLA: 5.9 ± 0.2 KJ/m²
Charpy impact strength	- KJ/m²
Elongation at break	(ASTM D638) Model White LCD/DLP: 6.9 ± 1.1 / Model Clear LCD/DLP: 6.4 ± 2.2 / Model Grey LCD/DLP: 6.2 ± 2.1 / Model Black LCD/DLP: 5.9 ± 1.5 / Model White SLA: 5.9 ± 2.1 / Model Clear SLA: 5.9 ± 3.1 / Model Grey SLA: 6.1 ± 2.1 %
Tensile strength	(ASTM D638) Model White LCD/DLP: 40.2 ± 2.3 / Model Clear LCD/DLP: 37.0 ± 4.0 / Model Grey LCD/DLP: 41.8 ± 2.3 / Model Black LCD/DLP: 40.8 ± 4.3 / Model White SLA: 39.2 ± 4.3 / Model Clear SLA: 38.6 ± 2.4 / Model Grey SLA: 45.2 ± 4.3 MPa
Tensile modulus	- MPa
Flexural strength	(ASTM D790) Model White LCD/DLP: 74.3 ± 3.5 / Model Clear LCD/DLP: 69.2 ± 3.7 / Model Grey LCD/DLP: 73.8 ± 3.7 / Model Black LCD/DLP: 75.2 ± 5.1 / Model White SLA: 69.3 ± 4.3 / Model Clear SLA: 66.3 ± 5.2 / Model Grey SLA: 74.3 ± 4.7 MPa
Flexural modulus	(ASTM D790) Model White LCD/DLP: 2190 ± 240 / Model Clear LCD/DLP: 1678 ± 157 / Model Grey LCD/DLP: 1700 ± 200 / Model Black LCD/DLP: 1607 ± 164 / Model White SLA: 1998 ± 197 / Model Clear SLA: 1791 ± 171 / Model Grey SLA: 2016 ± 198 MPa

Thermal properties
Softening temperature	50 ºC

Specific properties
Maximum water absorption	(ASTM D570) 24 h: 0.47 %

Other
HS Code	2916.1
Lifetime (since manufacturing)	24 M

Once a print is finished, the part of the manufacturing platform must be removed with the metal spatula, being careful not to damage the surface of the platform. Then, the piece is immersed in IPA for 5 - 15 minutes, depending on the color of the resin and the size of the piece, to remove the non-solidified resin from those of the outer walls of the piece. After that time, pressurized air should be applied to the piece until it is completely dry. To achieve the maximum properties that HARZ Labs Model Resin can provide, it is necessary to cure the resin for 15 - 30 minutes at a temperature of 40 - 60 ºC (eliminate internal stresses) in a curing center (Form Cure) that has a wavelength 405 nm.

Before removing the parts from the manufacturing base, the user must be equipped with a series of safety measures. The use of gloves is recommended to prevent the resin and alcohol from coming into contact with the skin, it is also crucial to wear safety glasses for the drops that may originate during the washing of the pieces.