Fiberon PA6-GF25 1.75 mm 500 g
search
  • Fiberon PA6-GF25 1.75 mm 500 g
  • Fiberon PA6-GF25 1.75 mm 3 kg
Compare
You must be logged in to manage your wishlist.

Fiberon PA6-GF25

FIBERON-PA6GF25-GREY-175-500
28.92 € 28.92 €
Tax excl.
Diameter
Format
Colour
Quantity

In stock 0 units available for immediate shipping.
units available for shipping in 15 - 21 days Available for shipment within 15 - 21 days

Product temporarily out of stock with these characteristics. Select another combination.

Product temporarily out of stock with these characteristics. Select another combination.

We notify you when it will be available:

Approximate delivery date: Thursday 12 December - Friday 20 December
Available

The PA6-GF25 filament is a high-performance composite filament from the Fiberon line, made from a PA6 base with a 25% glass fiber load. This filament offers exceptional thermal and mechanical properties while ensuring excellent printability and strong layer adhesion. Known for its strength and durability, it boasts a heat deflection temperature of 191 ºC. PA6-GF25 is ideally suited for applications that require stiffness, durability, and heat resistance, making it an excellent choice for consumer products, electronics, and industrial parts. Its enhanced material properties ensure high performance in demanding environments.

Part 3D printed with the PA6-GF25 filament

Image 1: Part 3D printed with the PA6-GF25 filament. Source: Fiberon.

The PA6-GF25 filament offers a combination of enhanced material properties and easy-to-use printing features, such as minimal creep and the ability to perform high-speed printing at rates up to 300 mm/s. This filament does not require a heated chamber, allowing for consistent results at ambient temperatures. It is ideal for 3D printers designed for composite material extrusion, including models like the Raise3D E2CF and the Bambu Lab X1C. Additionally, PA6-GF25 is compatible with multimaterial systems, such as Bambu Lab's AMS module. For optimal durability and consistent printing performance, using an abrasion-resistant nozzle is recommended.

A mould 3D printed with the PA6-GF25 filament

Image 2: A mould 3D printed with the PA6-GF25 filament. Source: Fiberon.

To boost the thermal and mechanical performance, PA6-GF25 parts should undergo a 100 ºC annealing process for 16 hours. This process requires careful handling to prevent deformation. Guidelines include waiting 24 hours after printing (or drying at 80 ºC for 2 hours) to relieve internal stresses, ensuring uniform oven temperatures, and adding supports (PolyDissolve S1) for parts with overhangs, thin walls, or bridging structures. For optimal results, parts should be placed in the oven in the same orientation as during printing, ideally on the build plate itself, ensuring precise dimensional accuracy and long-term stability.

General information
Material PA
Format 500 g / 3 kg
Density (ISO 1183) 1.20 g/cm³
Filament diameter 1.75 mm
Filament length (Ø 1.75 mm-0.5 Kg) ±173.2 m / (Ø 1.75 mm-3 Kg) ±1039.4 m

Electrical properties
Surface electrical resistivity (ANSI ESD S11.11) OL, > 10¹² Ohm

Printing properties
Printing temperature 280 - 300 ºC
Print bed temperature 40 - 50 ºC
Chamber temperature 20 - 25 ºC
Cooling fan ✗
Recommended printing speed Max. 300 mm/s
Recommended nozzle Hardened Steel

Mechanical properties
Charpy impact strength (ISO 179) 10.0 ± 0.7 KJ/m²
Elongation at break (ISO 527) XY: 2.4 ± 0.2 % / Z: 4.0 ± 0.4 %
Tensile strength (ISO 527) XY: 80.1 ± 1.8 MPa / Z: 60.7 ± 1.1 MPa
Tensile modulus (ISO 527) XY: 5356.9 ± 211.0 MPa / Z: 3375.9 ± 142.1 MPa
Flexural strength (ISO 306) XY: 133.8 ± 4.7 MPa / Z: - MPa
Flexural modulus (ISO 178) XY: 4314.22 ± 120.6 MPa / Z: - MPa
Surface hardness -

Thermal properties
Melting temperature (DSC) 214.5 ºC
Softening temperature - ºC
Heat deflexion temperature (ISO 75) @ 0.45 MPa: 191 ºC / @ 1.8 MPa: 157 ºC

Specific properties
Transparency ✗
Flammability classification UL 94 HB @ 1.5 mm
Chemical resistance ✓

Other
HS Code 3916.9
Spool diameter (outer) (0.5 kg) 200±1 mm / (3 kg) 250±1 mm
Spool diameter (inner hole) (0.5 kg) 55±1 mm / (3 kg) 55±1 mm
Spool width (0.5 kg) 65.6±2 mm / (3 kg) 117.2±2 mm

To achieve optimal print quality with the Fiberon PA6-GF25 filament, it is recommended to set the extrusion temperature between 280-300 ºC, and the print bed should be maintained between 40-50 ºC. It must be kept in mind that printing on a hotter bed will deactivate the Warp-Free technology. A room temperature for the build chamber is sufficient, and it is best to keep the cooling fan turned off. Fiberon PA6-GF25 supports high-speed printing with speeds of up to 300 mm/s, making it suitable for projects where efficiency is crucial.

Proper filament storage is essential for maintaining the quality of Fiberon PA6-GF25. To prevent compromised print quality due to moisture, it should be stored in a sealed container with desiccant. If the filament absorbs excess moisture, drying it at 100 ºC for 10 hours in a filament dryer is recommended (or PolyDryer at level 3 for 18 hours) to restore its optimal printing properties.

Since the Fiberon PA6-GF25 filament contains abrasive carbon fibers, it is highly recommended to use an abrasion resistant nozzle (hardnened steel, vanadium, ruby tip, etc) to avoid its excessive wear and, in consequence, inferior part quality.

Featured properties

Printing temperature
280 - 300 ºC
Filament diameter
1.75 mm
High speed compatible
Yes
Density
1.20 g/cm³