  • zENG (UniZ) View larger

    zENG (UniZ)

    SL-ZENG-AMBER

    Uniz Technology

    This product could be delivered in a period exceeding the standard.

    New product

    126,00 €tax excl.
    152,46 €tax incl.

    Ask for information

    Material with good mechanical properties that fits the vast majority of industrial applications.

    In the engineering sector always seeks to optimize the models that are manufactured with optimized designs and materials suitable for each application. Since UniZ have developed zENG resin, a material with good mechanical properties that fits the vast majority of applications that an industrial technician needs.

    The zENG resin has a high ductility and impact resistance without sacrificing surface quality. These advanced mechanical properties are perfect to carry out final pieces within any industry, such as: tools, conduits, housings and protections.

    The LED-LCD technology used by UniZ joins the other two technologies of 3D resin priniters already known, SLA and DLP. Its operation is similar to DLP, solidifying each layer in a single beam of light, but in the case of 3D LED-LCD printers, a set of LEDs with a wavelength of 405 nm illuminates an LCD screen that lets the beam pass through of light with the shape of the layer that is being manufactured.

    The zENG resin for 3D printing LED-LCD of UniZ is available in Amber color, a strong yellow with a certain percentage of translucency, which offers the user a vision of what happens inside a piece. This application is very common when making molds in two parts, as you can see in the following image.

    Mold created with zENG

    Image 1: Mold created with zENG. Source: UniZ

    The bottle of this UV resin has a volume of 500 ml and a system of operation by suction. This system, combined with the pump of the SLASH 3D resin printer, allows to discharge and load the resin in the bottle, which is very useful when storing the resin. It is recommended to store the resin in the bottle if a time of non-operation of more than three days is estimated, for that simply press the button to load the bottle in the rolling software until the tank is without resin, place the stopper in the aeration hole and remove the bottle. To complete the cycle, it is necessary to clean the circuit with the cleaning bottle with isopropyl alcohol inside.

    Botella de limpieza

    Image 2: Clean bottle. Source: UniZ
    Impact strength (KJ/m2) 3.854
    Elongation at break (%) 39.5
    Tensile strength (MPa) 35.4
    Tensile modulus (MPa) 389
    Flexural strength (MPa) 56
    Flexural modulus (MPa) 1937
    Vibration resistance Vibration resistance
    Sealing Sealing
    Hide color variations (Hide color variations)

    Once an impression is finished, the piece should be removed from the base with the metal spatula that is included with the printer. Then the piece is immersed in IPA for 5-15 minutes to remove the uncured resin from the outer walls of the piece. After that time, pressurized air must be applied on the piece until it is completely dry. To achieve the maximum properties that the zABS resin can provide, it is necessary to cure the resin for 10 minutes in a curing center (Form Cure) having a wavelength of 405 nm.

    Before removing parts from the manufacturing base, the user must be equipped with a series of safety measures. It is recommended the use of gloves to prevent the resin and alcohol from coming into contact with the skin, it is also crucial to use safety glasses for the drops that may originate during the washing of the pieces.

    General information
    Manufacturer Uniz (San Diego, USA)
    Technology  LCD
    Material Photopolymer
    Wavelength UV 405 nm
    Format 500 ml
    Color Amber yellow
    Compatible 3D printers Slash+, Slash+ UDP, Slash Pro, Slash Pro UDP, Slash DJ2
    Print settings
    Layer height 10-25-50-75-100-150-200-300 microns 
    Exposure Time Although the values ​​can be modified, it is not necessary to configure the printing parameters in 3D Uniz printers because the software has the ideal values ​​for each type of resin and layer height.
    Off time
    Lifting height
    Bottom exposure
    Bottom layers
    Curing and washing properties
    Washing time 10 min
    Curing time 10 min
    Curing temperature 25ºC
    Mechanical properties (without curing / with curing)
    Izod impact strength (ASTM D 256-10) 38.54 J/m / 18.38 J/m
    Charpy impact strength -
    Elongation at break (ASTM D 638-14) 39.5% / 11.1%
    Tensile strength (ASTM D 638-14) 15.3 MPa / 35.4 MPa
    Tensile Modulus (ASTM D 638-14) 107.44 MPa / 389.69 MPa
    Flexural strength (ASTM D 790-15) 15.23 MPa / 56.18 MPa
    Flexural modulus (ASTM D 790-15) 570.44 MPa / 1937.61 MPa
    Surface hardness -
    Thermal properties
    Softening temperature -
    Additional Information
    Lifetime (since manufacturing) 12 months
    HS Code 2916.1


    * The typical values detailed in this table should be considered as a reference. Actual values may vary depending on the 3D printer model used, part design and printing conditions. We recommend confirming the results and final properties with own tests. For more information you should consult the technical data sheet of the product.