IND475 A60 High Rebound resin WHITE - Loctite 3D

View larger

IND475 A60 High Rebound resin - Loctite 3D

Reference:

Brand: Loctite

This product could be delivered in a period exceeding the standard.

Condition: New product

Format

Colour

Quantity

225,00 €

Ask for information

Elastomeric resin for flexible parts with a good balance of hardness, strength and elongation.

Add to wishlist

More info
Data sheet
Download
Usage tips
Specifications

The IND475 A60 High Rebound resin from the Loctite family of elastomeric resins is a single component elastomer material characterized by a good elongation at break (201 %) with a good level of hardness and strength, and low shrinkage during printing. Parts 3D printed with this resin offer a high energy return (55 %).

The IND475 A60 High Rebound resin is the perfect material for the additive manufacturing of functional prototypes, lattice structures, cushioning pads, flexible seals and housings, air and dust gasket, or any parts that require resilience, snapback and tear resistance.

A lattice structure 3D printed with the Loctite IND475 A60 High Rebound resin

Image 1: A lattice structure 3D printed with the Loctite IND475 A60 High Rebound resin. Source: Loctite.

The IND475 A60 High Rebound resin has been formulated to print optimally on industrial DLP printers. Before printing with this material, the user should read safety and technical information available in the Downloads section. In the Usage Tips section useful resources can be found on printer compatibility, recommended post-processing settings, and proper resin storage.

Elongation at break (%)	201
Tensile strength (MPa)	3.1
Tensile modulus (MPa)	1.1
Surface hardness	1
Elasticity	Elasticity

IND475 HR Datasheet

Download

IND475 HR Safety Datasheet

Download

On the Henkel YouTube channel, various videos are available on:

How to work with 3D printing resins:

Video 1: The basics of printing with resin. Source: Henkel.
How to properly store 3D printing resins:

Video 2: How to properly store resins. Source: Henkel.
How to post-process parts 3D printed with resin:

Video 3: Resin post-processing tips. Source: Henkel.

The material's technical and safety datasheets can be found in the Downloads section. On the manufacturer's website the user can find the printer validation information as well as the recommended printing and postprocessing settings.

General information
Manufacturer	Loctite
Technology	DLP
Material	Photopolymer
Wavelength	-
Format	1 kg 5 kg
Color	White
Compatible 3D printers	DLP
Printing properties
Layer height	-
Layer exposure time	-
Layer cooling time	-
Lifting height	-
Exposure of lower layers	-
Number of bottom layers	-
Curing and washing properties
Washing time	4 min
Curing time	5-90 min
Curing temperature	-
Mechanical properties
Izod impact resistance	-
Charpy impact resistance	-
Elongation at break (ASTM D638)	201 %
Tensile strength (ASTM D638)	3.1 MPa
Tensile modulus (ASTM D638)	1.1 MPa
Bending strength	-
Bending modulus	-
Surface hardness (ASTM D2240)	Shore 57 A
Thermal properties
Softening temperature	-
Brightness value	-
Electrical properties
Volumetric resistivity (ASTM D257)	8.95E +11 Ω·cm
Surface resistivity (ASTM D257)	2.53E +13 Ω
Dielectric strength (ASTM D149)	29.6 kV/mm
Additional information
Service life	-
HS Code	2916.1

* The typical values listed in this table should be considered as a reference. Actual values may vary depending on the 3D printer model used, part design and printing conditions. We recommend confirming the final results and properties with your own tests. For further information please refer to the product data sheet.