FCer ZrO2 - Colfeed4Print
search
  • FCer ZrO2 - Colfeed4Print
You must be logged in to manage your wishlist.

FCer ZrO2 - Colfeed4Print

COLFEED-FCER-ZRO2-175-10M
330.00 € 330.00 €
Tax excl.
Diameter
Format
Quantity

Do you need more than 1 units?
Please, contact us.

In stock 1 units available for immediate shipping.
units available for shipping in 0 - 0 days
Available for shipment within 0 - 0 days

Product temporarily out of stock with these characteristics. Select another combination.

Product temporarily out of stock with these characteristics. Select another combination.

We notify you when it will be available:

Approximate delivery date: Wednesday 20 November

Colfeed4Print's FCer family of materials includes the FCer ZrO2, an innovative filament with a PLA base and 3 mol.% yttria stabilized zirconia (Y-TZP) nanoparticles (78 wt.% / 42 vol.%). The standout feature of FCer ZrO2 lies in its ability to seamlessly transition from printed form to a 100% zirconia piece or scaffold by sintering at 1500 ºC. This remarkable capability opens doors to boundless possibilities, allowing for the creation of dense pieces and scaffolds with customized shapes. Crafted with precision, this filament is expertly formulated to facilitate the effortless fabrication of 100% inorganic parts through 3D printing. Its advanced composition enables the straightforward production of bone-inducing scaffolds, tailored to exact specifications.

Sintered (left) and green (right) samples, printed with the FCer ZrO2 filament

Image 1: Sintered (left) and green (right) samples, printed with the FCer ZrO2 filament. Source: Colfeed4Print.

Zirconia, also known as zirconium dioxide (ZrO2), is a crystalline oxide of zirconium. It is a white, ceramic material that is widely used in various industries due to its exceptional properties. Zirconia is renowned for its high strength, hardness, and resistance to wear and corrosion, making it valuable in applications where durability is critical. In medicine, zirconia offers numeorus benefits and constitutes a versatile and promising platform for tissue engineering and regenerative medicine applications, providing the necessary support and environment for effective tissue regeneration.

Cross-section of the FCer ZrO2 filament

Image 2: Cross-section of the FCer ZrO2 filament. Source: Colfeed4Print.

For optimal printing results, adhere to the following printing recommendations: maintain a printing temperature of 158-170 ºC, with a bed temperature ranging from 30-60 ºC. A printing speed of 10-20 mm/s and a layer height exceeding 0.15 mm are advised. To safeguard the integrity of the filament, store it in a dry, shaded environment within the temperature range of 5-30 ºC. Prior to printing, it is advisable to pre-dry the filament at 60 ºC for 2 minutes, mitigating the risk of filament irregularities such as popping or nozzle clogging. More 3D printing tips can be found in the technical datasheet and printing recommendations document in the Downloads section.

General information

Material PLA
Format 10 m
Density 3.23 g/cm³
Filament diameter 1.75 mm
Filament tolerance ±0.15 mm
Filament length 10 m

Printing properties

Printing temperature 158-170 ºC
Print bed temperature 30-60 ºC
Chamber temperature -
Cooling fan -
Recommended printing speed 10-20 mm/s
Recommended nozzle diameter Min. 0.4 mm

Mechanical properties

Elongation at break - %
Tensile strength - MPa
Tensile modulus - MPa
Flexural strength - MPa
Flexural modulus - MPa
Surface hardness -

Thermal properties

Melting temperature 153 ºC
Softening temperature - ºC

Specific properties

Transparency

Other

HS Code 3916.9
Spool diameter (outer) - mm
Spool diameter (inner hole) - mm
Spool width - mm
General Information
Manufacturer Colfeed4Print
Material PLA with zirconia particles
Format 10 m coil
Density 3.23 g/cm3
Filament Diameter 1.75 mm
Diameter Tolerance ±0.15 mm
Filament Length 10 m
Color -
RAL/Pantone  -
Printing Properties
Printing Temperature 158-170 ºC
Bed Temperature 30-60 ºC
Chamber Temperature -
Layer Fan -
Printing Speed 10-20 mm/s
Nozzle Diameter ≥ 0.4 mm
Mechanical Properties
Izod Impact Strength -
Charpy Impact Strength  -
Break Elongation -
Tensile Strength  -
Tensile Modulus  -
Flexural Strength  -
Flexural Modulus -
Surface Hardness -
Thermal Properties
Softening Temperature  -
Melting Temperature 153 ºC
Specific Properties
Transparency
Additional Information
HS Code 3916.9
Reel Diameter (outer) -
Reel Diameter (inner hole) -
Reel Width -


* The typical values detailed in this table should be considered as a reference. Actual values may vary depending on the 3D printer model used, part design, and printing conditions. We advise confirming the results and final properties with your own tests. For more information, please refer to the product's technical datasheet.

Featured properties

Printing temperature
158-170 ºC
Filament diameter
1.75 mm
Density
3,23 g/cm³