XYZ Standard Resin (DLP)

RESIN-XYZ-STD-DLP-CLEAR
139.67 € 139.67 €
Tax excl.
Colour
Quantity

In stock 0 units available for immediate shipping.
units available for shipping in 15 - 20 days Available for shipment within 15 - 20 days

Product temporarily out of stock with these characteristics. Select another combination.

Product temporarily out of stock with these characteristics. Select another combination.

We notify you when it will be available:

Approximate delivery date: Tuesday 10 December - Tuesday 17 December
Available

XYZ resins for 3D printing SLA technology have been developed for the XYZ Nobel Superfine printer and allow to achieve high levels of detail and precision in dental models, jewelry, art or prototypes.

Available in 3 colors, this resin provides a wide range of applications and a moderate rigidity, which makes it suitable for parts with functions mainly design prototypes for engineering.

Installing the bottle of resin is really simple and is done in just three steps: You must replace the cap, insert the bottle into the 3D printer and finally connect the tube. The material, color, and remaining resin level will automatically be detected and the tank will be automatically filled.

The package includes 2 bottles of 500ml, so the total amount is 1 liter.

If an UV curing unit of XYZ is available, it is necessary to select the power level 3 and the curing time 10. It is important to store the resin at a temperature of between 10 and 32 ° C to avoid deterioration thereof. In addition, you must have different tanks for each type of resin (material / color) to avoid printing failures.

General information
Manufacturer XYZprinting
Material Photopolymer
Format 2x 0.5 L
Density 1-1.2 g/cm³
Technology DLP
Wavelength -
Compatible 3D printers Nobel 1.0 / Nobel 1.0A / Nobel Superfine
Viscosity (@25 ºC) 190-950

Printing properties
Layer height - µm
Layer exposure time -
Layer off time -
Bottom layer exposure -
Bottom layer count -

Curing and washing properties
Washing time - min
Curing time - min
Curing temperature - ºC

Mechanical properties (uncured / cured)
Izod impact strength - KJ/m²
Charpy impact strength - KJ/m²
Elongation at break (ASTM D638) 0.1-10 %
Tensile strength (ASTM D638) 20 - 40 MPa
Tensile modulus (ASTM D638) 800 - 1900 MPa
Flexural strength (ASTM D790) 35 - 90 MPa
Flexural modulus (ASTM D790) 1400 - 2300 MPa
Surface hardness Shore 70 - 90 D

Thermal properties (uncured / cured)
Softening temperature 50 ºC

Other
HS Code 2916.1
Lifetime (since manufacturing) - M
  1. Heating of this product is strictly prohibited. Photopolymer resins can generate vapors that can cause discomfort when subjected to high temperatures.
  2. Keep the product in a well-ventilated space out of the reach of children.
  3. Avoid contact of skin or eyes with uncured resin. If accidental contact occurs, immediately rinse the affected area with clean water.
  4. The uncured resin in the tank can solidify if it is exposed to sunlight before it is removed. Therefore, be careful when disposing of uncured resin and do not pour the material directly into the sink.
  5. After printing, any uncured resin on the surface of the printed object should be cleaned with alcohol.

Featured properties

Technology
DLP