Taulman Nylon Bridge

Ref.: TLM-NYL-BRIDGE-175-1000

53.95 €

-25%

40.46 €

Tax excl.

Diameter

Format

Quantity

In stock 18 units available for immediate shipping.
units available for shipping in 0 - 0 days Available for shipment within 0 - 0 days

Product temporarily out of stock with these characteristics. Select another combination.

We notify you when it will be available:

Approximate delivery date: Friday 22 November

Available

Returns

Ask about this product

Taulman nylon Bridge (or polyamide) is a plastic of high available quality for the 3D printing. It is born with the end to be a filament “Bridge or union” between the high resistance and flexibility of the Taulman Nylon 645 and the price reduced of the ABS and the thermoplastic PLA. It is practically the same of resistant that the Taulman Nylon 645 but to his time is very flexible. It allows to any user print pieces with these characteristics of resistance and flexibility to an affordable price surpassing the current barriers of other filaments of nylon. This filament of nylon is produced by Taulman 3D especially for the 3D printed.

The main characteristics of the Taulman nylon Bridge are the following:

Greater adherence of the layer to the base of prints: One of the big advantages regarding other filaments nylon of other manufacturers is that introduce a big adherence to the base of print.
Decrease of the absorption of humidity: Although it is not possible to delete of the all the catchment of humidity in the 3D printing with Taulman Nylon locates this humidity in the surface of the piece, so that the piece does not require to be subjected to processes of dried after the print.
Reduction of the warping: The same process that reduces the catchment of humidity helps to reduce the warping. This is especially important since the Nylon has a sensitivity to the greater shrinkage that the ABS, by what the warping will be one of the greater factors to watch when it prints with Nylon. Nylon Taulman Reduces considerably this effect.
Transparency: Nylon Bridge has an opacity of 68%. To the equal that Taulman Nylon 645, Taulman Nylon Bridge allows, thanks to his transparency, the visual inspection of parts printed. Being transparent, Taulman nylon Bridge and Taulman 645, allow the no destructive evaluation of the piece, even in his interior. If what looks for is a total transparency has to choose the Taulman T-Glase since it is his main virtue.

Besides it presents a practically invalid contraction, by what is besides a good material to print big pieces.

General information
Material	PA
Format	50 g / 450 g / 1000 g
Density	1.25 g/cm³
Filament diameter	1.75 / 2.85 mm
Filament tolerance	± 0.05 mm
Filament length	(Ø 1.75 mm - 0.45 Kg) ± 149 m / (Ø 2.85 mm - 0.45 Kg) ± 56 m

Printing properties
Printing temperature	250 - 255 ºC
Print bed temperature	30 - 65 ºC
Chamber temperature	30 - 100 ºC
Cooling fan	✗
Recommended printing speed	- mm/s

Mechanical properties
Elongation at break	248 %
Tensile strength	33 MPa
Tensile modulus	183 MPa
Flexural strength	- MPa
Flexural modulus	- MPa
Surface hardness	-

Thermal properties
Melting temperature	217 ºC
Softening temperature	52 ºC

Specific properties
Transparency	32 %
Flammability classification	UL 94 HB

Other
HS Code	3916.9
Spool diameter (outer)	200 mm
Spool diameter (inner hole)	50 mm
Spool width	50 mm

It is advisable that the printer dock is warm with placing BuildTak or Kapton Tape for which adheres well and thus achieve a better result print (Minimize the most of the warping effect). The recommended temperature of 252 ° C extruder is.

During the printing process can you see smoke coming from the extruder, do not panic, it's just water vapor. This is because the nylon has a great capacity to absorb moisture. For this reason we recommend that after use in your 3D printer save your spool nylon bag with the absorbent silica in the original bag. Close the bag so that it is the best possible sealed and store in a dry place.