Prusament PA11 (Nylon) Carbon Fiber

Ref.: PRUSA-PA11-CF-K-175-800G

90.90 €

Tax excl.

Diameter

Format

Colour

Quantity

In stock 0 units available for immediate shipping.
units available for shipping in 5 - 9 days Available for shipment within 5 - 9 days

Product temporarily out of stock with these characteristics. Select another combination.

We notify you when it will be available:

Approximate delivery date: Monday 15 September - Friday 19 September

Available

Returns

Ask about this product

The PA11 Carbon Fiber filament from Prusa3D is an advanced engineering solution for FDM 3D printing, designed to offer extreme strength in high thermal, chemical, and mechanical demand environments. Made from polyamide 11 reinforced with recycled carbon fibers, this technical material provides an exceptional combination of structural rigidity, low warping, and durability, making it ideal for professional applications in sectors such as automotive, aerospace, and functional engineering.

Thanks to its heat resistance of up to 190 °C, high dimensional stability, and excellent performance against industrial solvents like acetone, methanol, or oils, PA11 with carbon fiber enables the production of parts exposed to critical conditions. Its matte black surface also delivers a professional finish, while its low coefficient of friction and good wear resistance make it an ideal alternative for functional components, brackets, guides, and mechanical parts subject to friction or continuous stress.

Photo 1: Prusament PA11 Nylon Carbon Fiber withstands temperatures up to 190 °C, making it an excellent option for functional parts exposed to high thermal loads in professional applications. Source: Prusa3D

Unlike other polyamides, this filament is less hygroscopic, reducing the need for constant drying and improving long-term print quality. It exhibits minimal shrinkage during manufacturing, making it suitable for printing large parts without an enclosure. However, its use requires certain technical conditions: a hardened steel nozzle is essential due to its abrasiveness, and it is recommended to use a dedicated nylon print sheet or a separation layer to ensure proper bed adhesion.

Due to its excellent impact, tensile, and thermal resistance, this technical nylon filament allows for the creation of functional prototypes and end-use parts that meet the demands of industrial environments. It is a highly specialized option for those seeking performance, reliability, and precision in advanced 3D printing.

Photo 2: Thanks to its high strength and durability, Prusament PA11 Nylon Carbon Fiber is ideal for manufacturing parts exposed to demanding mechanical stress. Source: Prusa3D

Advantages and Considerations of PA11 Carbon Fiber Filament

This technical filament offers unique advantages over conventional materials but also requires certain conditions for optimal use. The table below summarizes its key pros and technical considerations.

Pros	Cons
✅ Withstands up to 190 °C	❌ Requires special print surface
✅ High resistance to industrial solvents	❌ Needs hardened steel nozzle
✅ Very low coefficient of friction	❌ Lower interlayer adhesion than pure PA
✅ High mechanical durability	❌ Occasional drying required
✅ Absorbs moisture very slowly	❌ Sensitive to high humidity environments
✅ Professional matte black finish	❌ Higher price than other filaments
✅ Very low shrinkage during printing	❌ Noticeable smell during printing

Photo 3: Thanks to its high strength and durability, Prusament PA11 Nylon Carbon Fiber is ideal for manufacturing parts exposed to demanding mechanical stress. Source: Prusa3D

Technical Specifications of PA11 Carbon Fiber Filament

These are the technical properties and recommended print settings for optimal performance of the PA11 filament reinforced with carbon fiber.

Parameter	Value
Base material	PA11 with recycled carbon fiber
Nozzle temperature	285 ± 10 °C
Bed temperature	110 ± 10 °C
Thermal resistance	Up to 190 °C
Chemical resistance	High (solvents, oils, fuels)
Abrasiveness	High – hardened nozzle required
Print speed	Fast
Print difficulty	Medium to high
Elasticity	Low
Post-processing	Easy (dry or wet sanding)
Color	Matte black
Odor during printing	High

Conclusion

The PA11 Carbon Fiber filament is one of the most durable and sustainable solutions on the market for technical 3D printing. Its polyamide composition with recycled carbon delivers high-performance parts for real industrial conditions. Designed for precision, durability, and strength, this material raises the standard for advanced manufacturing.

Photo 4: The combination of mechanical strength and creep resistance makes Prusament PA11 Nylon Carbon Fiber perfect for functional parts directly integrable into production environments. Source: Prusa3D

General information
Material	PA CF
Format	800 g \| 25 g
Density	(ISO 1183) 1.11 g/cm³
Filament diameter	1.75 mm
Filament tolerance	0.04 mm
Filament length	[800 g] 299.6 m \| [25 g] 9.4 m

Printing properties
Printing temperature	285 ºC
Print bed temperature	110 ºC
Cooling fan	20%
Recommended printing speed	Up to 100 mm/s
Recommended nozzle	Hardened Steel

Mechanical properties
Charpy impact strength	(ISO 179-1 Notched) 12 KJ/m²
Elongation at break	(ISO 527-1) 3.3 %
Tensile strength	(ISO 527-1) 42 MPa
Tensile modulus	(ISO 527-1) 25000 MPa
Flexural strength	(ISO 178) 63 MPa
Flexural modulus	(ISO 178) 63000 MPa
Surface hardness	(Prusa Polymers Shore D) 77