Zortrax Z-NYLON

Ref.: ZORTRAX-ZNYLON-BLACK-800

53.00 €

Tax excl.

Diameter

Format

Colour

Quantity

In stock 0 units available for immediate shipping.
units available for shipping in 4 - 8 days Available for shipment within 4 - 8 days

Product temporarily out of stock with these characteristics. Select another combination.

We notify you when it will be available:

Out of Stock

Returns

Ask about this product

Zortrax is a Polish company founded in 2013 and focused on the development of professional 3D printing systems. Its main strength is the excellent optimisation and integration between its 3D printers, materials and software. This greatly simplifies the entire printing process, minimising set-up times and reducing the likelihood of failure to a minimum, making them ideal systems for professional environments.

Zortrax offers a wide range of technical materials perfectly optimised for best results in conjunction with its LPD printers, including ABS, ASA, PCABS, Nylon, HIPS and others.

Z-NYLON is a high quality polyamide 12 filament, ideal for the production of prototypes and functional components. It stands out for its excellent mechanical properties, moderate elasticity as well as high temperature resistance.

Motorbike brake handle printed with Z-Nylon

Image 1: Motorcycle brake lever produced with Z-Nylon. Source: Zortrax.

One of its main advantages is that it can be post-processed with the same tools used for post-processing metals. It also has a high chemical resistance including acids and caustics.

It is an ideal material for the production of tools, mechanical components or functional prototypes. Due to its high shrinkage during cooling, it is not recommended for high volume production or components requiring high dimensional stability.

General information
Material	PA
Format	800 g
Density	(ISO 1183) 1.027 g/cm³
Filament diameter	1.75 mm
Filament tolerance	- mm
Filament length	(0.8 Kg) ± 323 m / (2 Kg) ± 809 m

Printing properties
Printing temperature	260 ºC
Print bed temperature	75 ºC
Chamber temperature	✗
Cooling fan	-
Recommended printing speed	- mm/s

Mechanical properties
Izod impact strength	(ISO 180) 13 KJ/m²
Elongation at break	(ISO 527) 23 %
Tensile strength	(ISO 527) 33 MPa
Tensile modulus	- MPa
Flexural strength	(ISO 178) 38 MPa
Flexural modulus	(ISO 178) 781 MPa
Surface hardness	(ISO 868) Shore 62 D

Thermal properties
Melting temperature	(ISO 11357) 173 ºC
Softening temperature	- ºC

Specific properties
Transparency	-

Other
HS Code	3916.9
Spool diameter (outer)	- mm
Spool diameter (inner hole)	- mm
Spool width	- mm

Parts printed with Z-NYLON suffer from high shrinkage during cooling and are therefore very prone to warping during printing. This is why it is highly recommended to always use the optional HEPA cover during printing.

It is also a very hygroscopic material, so it should always be stored in an airtight container when not in use. For long print runs we recommend Printdry Pro or similar.