IND5714 resin - Loctite 3D

Ref.: RS-LOC-IND5714-GREY-1KG

225.00 €

Tax excl.

Format

Colour

Quantity

In stock 0 units available for immediate shipping.
units available for shipping in 5 - 7 days Available for shipment within 5 - 7 days

Product temporarily out of stock with these characteristics. Select another combination.

We notify you when it will be available:

Approximate delivery date: Wednesday 8 January - Friday 10 January

Available

Returns

Ask about this product

The IND5714 resin by Loctite is an industrial-grade high strength elastomer engineered to enable the additive manufacturing of parts with high rebound capabilities and remarkable repetitive strain resistance. With a low Shore hardness of 53 A complemented by outstanding features including excellent compression set and tear resistance, high elongation at break, and low modulus, IND5714 stands out as the preferred material across a broad spectrum of industrial elastomeric applications. The resin was engineered to be compatible with a broad range of DLP and LCD machines.

Parts 3D printed with the Loctite IND5714 resin

Image 1: Parts 3D printed with the Loctite IND5714 resin. Source: Loctite.

The IND5714 resin offers ease of processing thanks to the excellent H&S Rating, it is TPO-free and comes with low hazard labeling, ensuring both safety and compliance. The IND5714 resin's versatility extends to safe touch applications and soft robotics, as well as cushioning and dampening needs in various sectors (shock absorbers, gaskets, seals), and also sporting goods and consumer products.

Ensuring reliability, parts 3D printed with IND5714 resin have undergone rigorous heat aging experiments without load according to ASTM D3045, exhibiting outstanding results. Samples were exposed to defined heat conditions, simulating real-world environments, and underwent mechanical testing according to ASTM D412, proving the material's durability and stability even under challenging conditions. The results can be consulted in the technical datasheet in the Downloads section.

Curing, washing, and sintering properties
Washing time	2 min
Curing time	10 min
Curing temperature	- ºC

General information
Manufacturer	Loctite
Material	Photopolymer
Format	1 kg
Technology	DLP/LCD
Wavelength	- nm
Viscosity	(ASTM D7867) @ 25 ºC: 2700 cP
Density (solid)	(ASTM D792) 1.04 g/cm³
Density (liquid)	(ASTM D1475) 1.01 g/cm³

Mechanical properties
Izod impact strength	- KJ/m²
Charpy impact strength	- KJ/m²
Elongation at break	(ASTM D638) 130-143 %
Tensile strength	(ASTM D638) 1.4 MPa
Tensile modulus	(ASTM D638) 4.1-4.9 MPa
Flexural strength	- MPa
Flexural modulus	- MPa
Surface hardness	(ASTM D2240) Shore 53 A
Compression	(D395-B) (22 ºC/24hr) 8-11 % / (70 ºC/24hr) 25-32 %

Printing properties
Layer height	- µm
Layer exposure time	-
Layer off time	-
Lifting height	- mm
Bottom layer exposure	-
Bottom layer count	-

Thermal properties
Softening temperature	- ºC

Specific properties
Maximum water absorption	(ASTM D570) 24 h: 3.5 % / 72 h: 5 % / 168 h: 5.3 %

Other
HS Code	2916.1
Lifetime (since manufacturing)	- M

On the Henkel YouTube channel, various videos are available on:

How to work with 3D printing resins:

Video 1: The basics of printing with resin. Source: Henkel.
How to properly store 3D printing resins:

Video 2: How to properly store resins. Source: Henkel.
How to post-process parts 3D printed with resin:

Video 3: Resin post-processing tips. Source: Henkel.

The material's technical and safety datasheets can be found in the Downloads section. On the manufacturer's website the user can find the printer validation information as well as the recommended printing and postprocessing settings.