Mt 316L

Ref.: MT-316L-NANOVIA-175-500

120.00 €

Tax excl.

Diameter

Format

Quantity

In stock 2 units available for immediate shipping.
units available for shipping in 0 - 0 days Available for shipment within 0 - 0 days

Product temporarily out of stock with these characteristics. Select another combination.

We notify you when it will be available:

Approximate delivery date: Thursday 26 December

Available

Returns

Ask about this product

316L Stainless Steel is a chromium nickel molybdenum, austenitic stainless steel with low carbon content. It is antimagnetic in its annealed state and cannot be hardened by heat treatment, but nevertheless has good forming properties, gaining strength by deformation. This has the disadvantage of requiring higher stresses to deform it. Its good ductility, tensile strength, heat resistance and corrosion resistance even at high temperatures, make 316L stainless steel used in many industrial applications: aeronautical industry as standard material, sectors that need metals resistant to the effects of salts and acids (paper, textile or chemical) or pharmaceutical industry to avoid metal contamination.

The Mt 316L filament allows dense stainless steel parts to be printed with a standard 3D printer which can then be sintered without the need for chemical debinding. After sintering, the result is a 100% stainless steel part.

Pieza impresa con Mt 316L

Image 1: Part printed with Mt316L. Source: Nanovia

Among the advantages of Mt 316L filament we can highlight:

Easy post-treatment before sintering.
No need for chemical debinding before sintering.
Alternative/complement to machining of parts.

To learn more about the sintering process, please refer to the "Tips for use" section or visit the manufacturer's website.

General information
Manufacturer	Nanovia
Material	Metal + binder
Format	50 g / 500 g
Density	7.19 g/cm³
Filament diameter	1.75 / 2.85 mm
Amount of filler (volume)	51 %
Amount of filler (mass)	87 %

Printing properties
Printing temperature	200 ºC
Print bed temperature	40 - 60 ºC
Recommended printing speed	20 - 40 mm/s
Recommended nozzle diameter	Min. 0.6 mm

Mechanical properties
Elongation at break	- %
Tensile strength	- MPa
Tensile modulus	- MPa
Flexural strength	- MPa
Flexural modulus	- MPa
Surface hardness	-

Thermal properties
Softening temperature	55 ºC

Sintering properties
Maximum temperature	1180 ºC

Other
HS Code	3916.9

Sintering

The sintering of Nanovia Mt Inox 316L filament occurs in two steps:

Debinding at a temperature around 400 °C
Sintering at 1180 °C

Temperature (°C)					0 – 425	425	425 – 1050	1050 – 1150	1150 – 1180	1180
Time (min)					213	240	313	200	300	1800

Nanovia Mt can be sintered in an SDS sintering furnace.
It is necessary to bury/cover the green parts in a crucible filled with alumina powder during the thermal debinding phase.
Add a thin layer of carbon powder to capture the released oxygen, or sinter using an inert atmosphere such as argon.