BASF Ultracur3D® EPD 1086

BASF-1086-BLACK
295.00 € 295.00 €
Tax excl.
Colour
Quantity

In stock 0 units available for immediate shipping.
units available for shipping in 4 - 6 days Available for shipment within 4 - 6 days

Product temporarily out of stock with these characteristics. Select another combination.

Product temporarily out of stock with these characteristics. Select another combination.

We notify you when it will be available:

Approximate delivery date: Friday 22 November - Tuesday 26 November
Available

BASF is a German manufacturer specialising in the development of chemical products. Its product range includes products for the production of 3D printing materials for FDM, resin and SLS.

Ultracur3D® EPD 1086 resin is a resin for daylight resin technology, i.e. for use in visible light printers such as Photocentric printers. Daylight is a lower energy, longer wavelength light that ensures more reliable polymerisation than UV light.

Photocentric has teamed up with BASF to create a range of Engineering Plastic Daylight (EPD) materials for a wide range of applications.

Ultracur3D® EPD 1086 black is a daylight resin with outstanding mechanical properties that enable a wide range of applications. In addition, one of its strengths is that parts printed with these resins are highly rigid and flexible.

Piezas impresas con ultracur 1086Image 1. Part printed with Ultracur3D® EPD 1086 resin. Source: Forward-am

It is also a low-cost solution for the manufacture of highly detailed or textured tools, utensils or parts.

Curing, washing, and sintering properties
Washing time -
Curing time -
Curing temperature - ºC

General information
Manufacturer BASF
Material Photopolymer
Format 5 kg
Technology EPD
Wavelength - nm
Viscosity @ 30 ºC: 450 mPa·s / @ 50 ºC: 130 mPa·s
Density (solid) (ASTM D792) 1.18 g/cm³

Mechanical properties
Izod impact strength - KJ/m²
Charpy impact strength (ISO 179-1) 2.6 KJ/m²
Elongation at break (ASTM D412C) 26 %
Tensile strength (ASTM D412C) 42 MPa
Tensile modulus 1810 MPa
Flexural strength (ASTM D790) 67 MPa
Flexural modulus (ASTM D790) 1620 MPa
Surface hardness (D2240) Shore 81 D

Printing properties
Layer height - µm
Layer exposure time -
Layer off time -
Lifting height - mm
Bottom layer exposure -
Bottom layer count -

Thermal properties
Softening temperature 53 ºC
Flammability classification (UL 94) HB @ 1.5 mm
Heat deflexion temperature (ASTM D648) @ 0.45 MPa: 53 ºC / @ 1.82 MPa: 46 ºC

Specific properties
Maximum water absorption (ASTM D570) 24 h: 0.23 %

Other
HS Code 2916.1
Lifetime (since manufacturing) 12 M

Before starting a print, the resin should be shaken well and, if possible, vacuumed to remove any bubbles that may have formed.

Once printed, the pieces should be cleaned with isopropyl alcohol. To do this it is advisable to immerse the pieces in a container with isopropyl alcohol and place this container in an ultrasonic cleaner for 4 minutes. It is recommended not to immerse the piece for long periods of time to avoid deformation and softening.

After cleaning, the pieces should be dried for 30 minutes at 40 ºC. Once dry, parts printed with BASF Ultracur3D resins should be cured at room temperature to obtain optimum properties. Curing conditions will depend on the characteristics of the printer used and the curing equipment.