Advanced resins for 3D printing

Advanced resins for 3D printing

One of the main barriers that 3D resin printing has always had when implemented at an industrial level has been the limited variety of materials available. Originally the only materials available were resins based on acrylate oligomers, generally of low molecular weight, which stood out for their high fragility and poor mechanical and thermal properties. Because of this, 3D resin printing has always been relegated to the background in the production of functional components and prototypes, in favour of thermoplastic-based 3D printing technologies such as FDM or SLS.

However, in recent years this has changed dramatically. The emergence of new technical resins with advanced properties and developed specifically for certain professional applications has brought this technology to the attention of many sectors. Coupled with the emergence of new resin-based 3D printing technologies such as LED-LCD, which have succeeded in reducing costs and significantly increasing printing speed, this is a viable alternative, which may even surpass FDM and SLS in some application areas.

These technical resins can be classified into three groups, depending on the field they are focused on:

  • Resins for jewellery
  • Dental Resins
  • Engineering resins

RESINS FOR JEWELLERY


The jewellery industry has historically been the first to implement 3D resin printing. This is due to the high resolution offered by this technology, capable of producing small 1:1 scale models with high quality finishes.

anillo uniz

Image 1: Jewellery model printed in resin. Source: uniz.com

Although standard resins are widely used for the production of models, what has meant a before and after has been the emergence of high quality castable resins. These resins stand out for leaving hardly any residues during calcination, which has made them a perfect substitute for the wax models originally used in casting.

Thanks to this it is possible to print the casting tree directly, without the need to make moulds to produce the wax masters or manually assemble the trees, which reduces the manual stages and automates the process.

Video 1: traditional preparation of a wax tree. Source: greekerajewelry.com

In general, this type of resin can include a percentage of liquid wax in its composition which is intended to eliminate any ash residues, producing a clean mould, suitable for quality casting. A higher percentage of wax will produce a cleaner calcination, and with less residue, however, it can affect printing precision. In addition, this type of resin is usually characterised by a very low coefficient of expansion.

There are currently many options on the market for high quality calcinable resins, compatible with both SLAs and DLPs or LED-LCDs. Formlabs "Castable Wax" resins with 20% wax or ZWax Purple with 10% wax and compatible with DLP and LED-LCD printers stand out for their combination of low residue, low thermal expansion and high precision.

zwax purple

Image 2: Ring printed with zWax Purple. Font: Uniz.com

DENTAL RESINS


Along with jewellery, the dental sector was one of the first to adopt 3D resin printing, and is now the fastest growing sector with the widest range of materials.

Dental resins can generally be grouped into four categories according to their application:

  • Resins for dental models.
  • Resins for retainers and splints.
  • Resins for temporary crowns and bridges
  • Burnable resins


Resins for dental models

These are resins that are not designed to be in contact with the patient. They are generally used for the production of patient models on which the dental or medical professional can work in order to plan interventions or to test elements such as crowns or bridges. They are similar in composition to standard resins and are mainly intended to have a high precision and resolution, as well as a low production cost.

modelo paladar

Image 3: 3D printed model with resin. Source: Uniz.com

It is also important in these resins that they have certain aesthetic qualities, distinguishing two groups:

  • Resins with a matt finish, which facilitate the visualisation and photography of the models, avoiding the appearance of reflections as much as possible. Among this type of resin, the Dental Model resin by Formlabs stands out, with a finish similar to plaster.
  • Resins that provide a realistic appearance, such as Dental Pink resin from Harzlabs.


Resins for retainers and splints

These resins are intended for the manufacture of retainers and splints, therefore, in addition to having a biocompatibility of at least class IIa, they must have an excellent resistance to wear and fracture.

Another common characteristic is that they tend to be highly transparent, mainly for aesthetic reasons.

Video 2: Manufacture of splints using 3D resin printing. Source: Formlabs.com

In addition to the production of retainers and splints, they are widely used in the manufacture of surgical guides due to their good compatibility and excellent mechanical properties. Some manufacturers such as Formlabs include a specific resin for this application such as Dental Surgical Guide resin, which provides greater flexibility.

guia quirurgica

Image 4: Surgical guides printed using SLA. Source: Formlabs.com

It is possible to find resins developed for the production of splints and retainers compatible with both SLA such as Formlabs Dental LT, and DLP and LED-LCD such as Dental Clear from Harzlabs.

Resins for temporary crowns and bridges

These are resins used to produce bridges, crowns, restorations and temporary veneers. They must be biocompatible and provide a finish similar to that of the original teeth.

To provide this finish in general, ceramic components and stains are used which provide shades within the VITA scale.

escala vita

Image 5: VITA colour chart. Source: vita-zahnfabrik

Once printed, these resins can be polished and shaded with light-curing veneers to obtain the ideal finish for each patient.

The Temporary CB resin by Formlabs is available in four VITA shades (A2, A3, B1 and C2) and the Dental Sand resin by Harzlabs is available in A1 and A2 shades.

Calcinable Resins

Resins similar to those used in jewellery. In this case, the need to produce as little waste as possible is even more critical.

They are mainly used in the production of models for the manufacture of dental implants by casting. The Harzlabs Dental Cast resin stands out, with a residue of less than 0.1 %.

ENGINEERING RESINS

The industrial and engineering sector has always been the most reluctant to implement 3D resin printing. This is mainly because, on a mechanical and thermal level, resins cannot compete with the engineering materials available for FDM or the polyamides used in SLS.

Although this is still true today, in recent years advances in materials and the emergence of new engineering resins are closing the gap between different 3D printing technologies. There are three groups of engineering resins:

  • Resins with improved mechanical properties
  • Resins with improved thermal properties
  • Flexible and elastic resins

Resins with improved mechanical properties


These are resins developed with the aim of providing lower fragility and higher modulus than standard resins. While standard resins such as Harzlabs Basic Resin offer a tensile strength of 20 MPa, new engineering resins such as BASF's Ultracur3D RG50 provide a tensile strength of up to 68 MPa, three times higher. This tensile strength is even higher than that provided by ABS filaments and close to materials such as load-reinforced nylon.

Engineering resins with other specific properties, such as high wear resistance or impact resistant resins, have also appeared.

tabla impacto

Image 6: Impact resistance comparison of various Formlabs resins. Source: Formlabs.com

Among the resins with high impact resistance, BASF's Ultracur3D High Impact line stands out. These resins provide a tensile strength of 50 MPa with a breakage deformation of 56%, a flexural modulus of 1700 MPa and an impact resistance of 1.39 J/m2. This makes them ideal for the production of mechanical components and functional prototypes.

ultracur3d rg35

Image 7: BASF Ultracur3D RG35 resin. Source: forward-am.com

Resins with improved thermal properties


Thermal resistance has always been one of the weak points of 3D printing resins. In general, all resins have softening temperatures between 50°C and 80°C.

tabla hdt

Image 8: Comparison of the heat deflection temperature of various Formlabs resins. Source: Formlabs.com

Currently, there are very few resins available for high temperature applications, with Formlabs' High Temp resin being the most important. This is a resin capable of withstanding temperatures of up to 142 ºC once cured (under a load of 0.45 MPa). The main advantage of this resin is that it is possible to increase its thermal resistance up to 238 ºC by applying a heat treatment to the parts consisting of heating them to 60 ºC for one hour and then to 160 ºC for one and a half hours.

Flexible and elastic resins


One of the main handicaps of 3D printing resins has always been their high brittleness, a property not desired in engineering. This is why the appearance in recent years of flexible and elastic resins has been a revolution.

Image 9: Comparison of Flexible 80A resin and Elastic 50A resin Source: FormLabs.

Today there are multiple options for both SLA and LED-LCD. In SLA, the flexible 80A and elastic 50A resins stand out. Flexible 80A is a highly flexible resin with 120% deformation at break and 80 Shore A hardness, while Elastic 50A is a resin with good elasticity, 160% deformation at break and 50 Shore A hardness.

However, one of the most important leaps forward in this type of material is BASF's new line of flexible and elastic resins. These are resins based on urethane acrylate oligomers, and offer the greatest flexibility and elasticity among the resins available today. BASF Ultracur3D FL300, for example, with a hardness of only 37 Shore A, provides breakage deformation of up to 306%.

ultracur3d fl60

Image 10: BASF Ultracur3D FL60 resin. Source: forward-am.com

In recent years, the range of materials for 3D resin printing has grown exponentially, including new materials with properties that match and in some cases even exceed those provided by thermoplastics for FDM. This, coupled with the fact that 3D resin printing provides superior isotropy to that obtained by FDM, makes it a viable option in many industrial and engineering applications.

Do you want to receive articles like this in your email?

Subscribe to our monthly newsletter and you will receive every month in your email the latest news and tips on 3D printing.

* By registering you accept our privacy policy.

1 Comments

  • Avatar
    mec
    dic 14, 2020

    Thank you. I got useful information for filament